Chlorinated Polyethylene CPE 135A as plastic additives
Model No.: | CPE 135A |
Min. Order: | 1 Metric Ton |
Payment Type: | L/C,T/T |
Transportation: | Ocean |
Productivity: | 1000MT/Month |
Packaging: | 25kg/bag |
Delivery Time: | 15 Days |
Place of Origin: | China |
Brand: | Gemhold |
Supply Ability: | 1000MT/Month |
Product Description
Chlorinated polyethylene (CPE, CPE 135A; CPE 135B and the various derivatives) is an inexpensive variation of polyethylene having a chlorine content from 34 to 44%. It is used in blends with polyvinyl chloride (PVC) because the soft, rubbery chlorinated polyethylene is embedded in the PVC matrix, thereby increasing the impact resistance. In addition, it also increases the weather resistance. Furthermore, it is used for softening PVC foils, without risking plasticizer migration. Chlorinated polyethylene can be crosslinked peroxidically to form an elastomer which is used in cable and rubber industry. When chlorinated polyethylene is added to other polyolefins, it reduces the flammability.
Application
CPE-135A is recommended to produce all kinds of opaque PVC products as PVC profiles, PVC fence, PVC pipe products, etc.
Product group characteristics
Performance
Indicator
Appearance
White powder
Volatile Content(%)
≤0.40
Heat of fusion(J/g)
≤2.0
Chlorine Content(%)
35±2
Sieve residue(0.9mm aperture)
≤2.0
Colored Particles (pieces/100g )
≤20
Tensile Strength(Mpa)
≥6.0
Shore A hardness(A)
≤65
Tg(°C)
1.1-1.2
Specific gravity
0.40-0.60
Bulk density(g/cm3)
≤5.0
CaCo3 content(%)
≤5.0
Reference formulation
Recommended using dosage:8.0-12.0kg per 100kg PVC resin.
Advantage
1. Excellent elongation rate at break and ductibility
2. Excellent compatibility with PVC resin
3. Good weather-resistance
4. Inherent flame-retardancy
5. Excellent heatproof, chemical-resistance and oil-resistance.
6. Excellent acceptance of high filler levels